 | American Society of Civil Engineers - Civil engineering - 1903 - 896 pages
...purpose the Vicat Needle, which has already been described in Paragraph 30, should be used. 40. — In making the test, a paste of normal consistency is moulded and placed under the rod (/,), Fig. 2, as described in Paragraph 31; this rod, bearing the cap (D) at one end and the needle... | |
 | Myron Samuel Falk - Cement - 1904 - 198 pages
...purpose the Vicat Needle, which has already been described in Paragraph 30, should be used. 40. — In making the test, a paste of normal consistency is...(L), Fig. 2, as described in Paragraph 31; this rod, bearinj the cap (D) at one end and the needle (//), I mm. (0.039 in.) in diameter, at the other, weighing... | |
 | Albert Bleininger - Cement - 1904 - 414 pages
...making the test, a paste of normal consistency is molded and placed under the rod (L) (figure 79), as described in paragraph 31; this rod, bearing the cap (D) at one end and the needle (H), i mm. (0.039 n1 -) ( n diameter at the other, weighing 300 gr. (10.58 oz.). The needle is then carefully... | |
 | Edwin Clarence Eckel - Cement - 1905 - 802 pages
...purpose the Vicat needle, which has already been described in Paragraph 30, should be used. 40. In making the test, a paste of normal consistency is moulded and placed under the rod, as described in Paragraph 31; this rod, bearing the cap at one end and the needle, 1 mm. (0.039 inch)... | |
 | Rolla C. Carpenter - Building materials - 1906 - 908 pages
...final set. For this purpose the Vicat needle, which has already been described, should be used. In making the test, a paste of normal consistency is moulded and placed under the rod (Z.), Fig. 100; this rod when bearing the cap (D) weighs 300 gr. (10.58 oz.). The needle (H), at the... | |
 | Richard Kidder Meade - Portland cement - 1906 - 422 pages
...molded and placed under the rod (L), Fig. 71, as described; this rod, bearing Fig. 71, Vicat Needle. the cap (D) at one end and the needle (H), 1 mm. (0.039 m.) 1n diameter, at the other, weighing 300 gr. (10.58 oz.). The needle is then carefully brought in... | |
 | Richard Kidder Meade - Portland cement - 1906 - 418 pages
...molded and placed under the rod (L), Fig. 71, as described; this rod, bearing Fig. 71, Vicat Needle. the cap (D) at one end and the needle (H), 1 mm. (0.039 m.) m diameter, at the other, weighing 300 gr. (10.58 oz.). The needle is then carefully brought in... | |
 | Hiram Bertrand Andrews - Reinforced concrete - 1908 - 68 pages
...described in paragraph 17, should be used. 22. In making the test, a paste of normal consistency is molded and placed under the rod (L), Fig. 2, as described in paragraph 18; this rod, bearing the cap (D) at one end and the needle (H), 1 mm. (0.039 in.) in diameter at the... | |
 | Louis Carlton Sabin - Cement - 1907 - 598 pages
...purpose the Vicat Needle, which has already been described in Paragraph 30, should be used. 40. In making the test, a paste of normal consistency is...described in Paragraph 31; this rod, bearing the cap (£>) at one end and the needle (//), 1 mm. (0.039 in.) in diameter, at the other, weighing 300 gr.... | |
 | American School (Lansing, Ill.) - Architecture - 1907 - 438 pages
...diameters. For this purpose the Vicat Needle, which has already been described, should be used. In making the test, a paste of normal consistency is...and placed under the rod L, Fig. 2, as described in a previous paragraph. This rod bears the cap D at one end and the needle H, 1 mm. (0.039 in.) in diameter,... | |
| |
In making the test, a paste of normal consistency is moulded and placed under the rod (L), Fig. 2, as described in Paragraph 31; this rod, bearing the cap (D) at one end and the needle (H), I mm. 